New insights into APCVD grown monolayer MoS2 using time

Scientific Reports volume 13,

Scientific Reports volume 13, Article number: 4146 (2023) Cite this article

1303 Accesses

Metrics details

In modern era, wireless communications at ultrafast speed are need of the hour and search for its solution through cutting edge sciences is a new perspective. To address this issue, the data rates in order of terabits per second (TBPS) could be a key step for the realization of emerging sixth generation (6G) networks utilizing terahertz (THz) frequency regime. In this context, new class of transition metal dichalcogenides (TMDs) have been introduced as potential candidates for future generation wireless THz technology. Herein, a strategy has been adopted to synthesize high-quality monolayer of molybdenum di-sulfide (MoS2) using indigenously developed atmospheric pressure chemical vapor deposition (APCVD) set-up. Further, the time-domain transmission and sheet conductivity were studied as well as a plausible mechanism of terahertz response for monolayer MoS2 has been proposed and compared with bulk MoS2. Hence, the obtained results set a stepping stone to employ the monolayer MoS2 as potential quantum materials benefitting the next generation terahertz communication devices.

The vision of wireless connectivity (Sixth generation connectivity, 6G) is drawing more and more attention due to its implications for the upcoming era of super smart society, artificial intelligence, virtual reality, smart wearable, autonomous vehicles, wireless local area networks (WLANs), high speed train (HST) communications and many more1,2,3. Idea behind 6G is to achieve the target of Tbps data transmissions with eco-friendly and green connectivity for the betterment of life quality for upcoming generation. As higher data traffic rate is mandatory in 6G wireless connectivity, introduction of underutilized terahertz (THz) frequency band is an important step4,5 by widening the operational band to THz frequency range and hence, doors for higher data rate and better spectral efficiency can be opened up. Typically, THz domain signifies the frequency band between microwave and optical frequencies as its spectral range lies between 100 GHz and 10 THz. This frequency range carries tremendous potential for deployment of novel futuristic technologies based on photonics as well as electronics. For real life application of the wireless communication system, suitable materials need to be utilized for related components which should be designed and assembled in efficient manner and compact in nature. Therefore, in search of desired THz materials, scientific community is now looking at newly emergent 2D materials that can replace existing bulk materials6. The atomically thin layered materials are considered exceptionally different due to their novel physical, chemical and electronic properties such as thermal stability, higher mobility, greater conductivity, bandgap tuneability, broadband optical response, and tuneable THz properties7. Thus, these materials exhibit great potential in dynamically controlling THz responsivity along with THz wave propagation7. Specific category of 2D materials i.e. transition metal diachalcogenides (TMDs) have captured significant attention because of stabilized carrier mobility and higher modulation efficiency. In this series, monolayer semiconducting TMDs with low dielectric screening reveal strongly bound excitons8. By using proper optical excitation, the excitonic properties of TMDs can be tuned in ultrafast reaction time of photoluminescence (PL)9. It is well established that the thinning down a bulk TMDs to monolayer or few layers, shifts the band gap from indirect to direct band gap10. Among all such TMDs, MoS2 could be the most suitable and promising candidate for THz applications because of its excellent electronic and photonic properties at room temperatures11,12,13,14. There are several methods to grow monolayer MoS2, out of which, the atmospheric pressure CVD (APCVD) approach is strongly favoured due to the most consistent, high quality, large production and cost-effective along with vacuum-free and continuous in-line processes.

In present investigations, highly reproducible triangular shaped monolayer MoS2 have been synthesised using indigenously developed low cost APCVD set-up at "CSIR-NPL" with calibration of zone temperature, maintaining required temperature gradient throughout the quartz tube. The commercially available CVD set-up is equipped with two zone furnace system including expensive MFC (mass flow controller), whereas we developed a single zone CVD furnace set-up that is cost-effective and equipped with a calibrated high precision rotameter to control the inert gas atmosphere in quartz tube for synthesizing highly reproducible monolayer MoS2. The quality of as-synthesized triangular shaped monolayer MoS2 were characterized and validated through several standard microscopic and spectroscopic techniques. The major focus of the present work is to explore the terahertz characteristics of monolayer MoS2 using time-domain terahertz spectroscopy and comparative study with bulk MoS2 which is not reported so far. Additionally, the plausible mechanism of terahertz characteristics associated with monolayer MoS2 has also been advocated in details to realize its potential usage in emerging next-generation terahertz communication devices as compared to bulk MoS2.

Monolayer MoS2 was successfully synthesized on SiO2/Si substrates using single step APCVD growth technique using indigenously developed set-up at "CSIR-NPL", New Delhi, India as shown in Fig. 1. Prior to the APCVD for growth of monolayer MoS2, all raw materials (MoO3 and S powder) utilized in the process were examined by XRD for purity and phase identification as shown in Fig. S1a,b. The quality growth, desired shape and size of monolayer MoS2 is dependent upon several important parameters such as growth time, growth temperature, heating rate, amount of gas flow and distance between the precursors15. The reaction of vapor phase includes two step process, first is formation of intermediate phase of MoO3-x during which sulfurization of oxide takes place as shown in Eq. (1), followed by further saturation of sulfurization to complete the proper substitution of sulfur in place of unsaturated oxygen atoms formed during the first intermediate reaction16,17.

Pictorial representations of (a) Indigenously laboratory developed APCVD setup for synthesis of monolayer MoS2. (b) Horizontal split furnace and quartz tube. (c) Arrangement of precursors and substrate inside the furnace at constant heating zone before growth and (d) after growth.

The following equation is obtained after combining above Eqs. (1) and (2):

In general, a complete sulfurization is essential for the growth of monolayer MoS2, while incomplete sulfurization is responsible for the growth of other secondary oxide phase (MoO2/MoO3) of molybdenum. To avoid the incomplete sulfurization, the rate of sulfurization can be controlled by changing the position of the sulfur boat to the center of heating zone, where the substrate was placed. Furthermore, by reducing proportion amount of sulfur to precursor (molybdenum oxide; MoO3) the growth of high-quality triangular shaped monolayer MoS2 can be controlled. Although, to optimize the condition, several statistical runs of APCVD were performed by varying the weight ratio of sulfur to MoO3 and different morphologies as well as size of monolayer MoS2 were deposited. The optimization of particular triangular shape has been done as reported in our previous studies15,18. The customized growth condition of present investigation has been discussed in details in experimental section. Further, to validate the number of layers of MoS2 in terms of qualitative analysis, Raman spectroscopy was performed. Prior to Raman spectroscopy, the shape, size (lateral dimension) and thickness contrast of as-deposited MoS2 layer on SiO2/Si substrate were probed by optical and field emission scanning electron microscopy (FESEM) techniques as shown in Fig. 2. The optical micrographs of as-deposited MoS2 layer on SiO2/Si at different magnifications have been shown in Fig. 2a–c. The morphologies of APCVD deposited MoS2 appear in triangular shape with maximum lateral size of 26.06 μm have been observed as shown in Fig. 2a and its contrast appears as atomically thin layer19. The maximum average lateral size is estimated to be 21.34 μm with number density of ~ 0.006/μm2 through FESEM as shown in Fig. 2d–f. The estimation of number density of monolayer MoS2 is described in details in the supporting note S2 and Fig. S2a,b (supporting information). The estimation of number density of monolayer MoS2 is based on selective area of FESEM image as shown in Fig. S2a. The statistical areal distribution of as grown monolayer MoS2 is shown in Fig. S2b. The lateral size of atomically thin triangular shape MoS2 obtained from FESEM is in agreement with lateral dimension obtained from optical micrographs as shown above. The same atomically thin triangular shape MoS2 sample has been used here from different selective areas for optical micrographs and FESEM. Raman spectroscopy has been performed to confirm the quality and number of layers of as deposited MoS2 by APCVD as shown in Fig. 3a. The Raman results exhibit the presence of two vibrational modes related to in-plane vibration of Mo and S atoms (E12g) at 381.57 cm−1, and out-of-plane vibration of S atoms (A1g) at 401.04 cm−1, respectively. The frequency difference (Δk) between E12g and A1g modes found to be 19.47 cm−1 at three different spatial positions of triangle selected randomly and the peak width estimated from full width half maxima (FWHM) of E12g mode which is found to be 4.76 cm−1 are in good agreement with the previously reported values of the APCVD-grown monolayer MoS218,20,21,22,23,24,25. Furthermore, Raman mapping has been performed to reveal the uniformity of vibrational modes throughout the triangular surface of as deposited monolayer MoS2. The Raman mapping images of the triangular surface of as deposited monolayer MoS2 evidence the uniform spatial distribution of Raman intensity for E12g and A1g vibration modes across the surface as shown in Fig. 3b,c. Thus, the Raman mapping confirms that the grown MoS2 layer, consisting of triangular shapes is monolayer in nature. Further, the absorption spectrum of monolayer MoS2 has been recorded for determination of optical transition as represented in Fig. S3. The UV–visible absorption spectrum and tauc plot of monolayer MoS2 have shown in Fig. S3a,b, respectively. The A excitonic peak (632 nm) emerges due to direct excitonic transition while B excitonic peak (612 nm) arises because of spin–orbit coupling as shown in Fig. S3a. Tauc equation has been employed to calculate the direct band gap of monolayer MoS2 which is 1.82 eV as shown in Fig. S3b.

where α: absorption coefficient, h: Planck's constant, ν: frequency, A: proportionality constant, Eg: band gap energy, γ: nature of electronic transition (for direct allowed transition, γ = 2)

Optical and FESEM Characterizations. (a–c) Optical images. (d–f) FESEM images at different magnifications of APCVD grown monolayer MoS2 over a 300 nm thick Si/SiO2 substrate, scale bar is mentioned.

Raman spectra and Raman mapping. (a) Raman spectra of triangular shaped monolayer MoS2 on 300 nm thick SiO2/Si substrate at three of its corners represented with their frequency difference of in and out of plane vibration modes. Raman mapping of triangular shaped monolayer MoS2with respect to vibrational peak intensity. (b) In plane E12g. (c) Out of plane A1g, scale bar is mentioned.

Furthermore, photoluminescence (PL) has been employed to analyse the quality of MoS2 monolayer at room temperature as shown in Fig. 4a. The PL spectra of triangular shaped MoS2 monolayer exhibits two distinct emission peaks upon excitation with diode laser of wavelength of 532 nm (2.33 eV). Among them, one of the strongest A excitonic emission peak is present in the range of 675 nm (1.83 eV) to 686 nm (1.80 eV) and centred at 680.86 nm (1.82 eV). While, another comparatively weak excitonic emission peak B exhibits in the range of 624 nm (1.98 eV) to 642 nm (1.93 eV), and centred at 633.82 nm (1.95 eV). The A and B excitonic emission peaks arise due to spin split direct transitions at K point of the Brillouin zone26,27,28,29. The PL emission intensity ratio of A to B excitonic peak was calculated to be 1.77 which again confirms the good quality of monolayer MoS2. The higher intensity of excitonic peak A than B implies the direct band transition in monolayer MoS2. Thus, the obtained PL result suggests that the quality of the MoS2 is monolayer in nature with direct band gap of 1.82 eV as compared to indirect bandgap of bulk MoS2 i.e.1.23 eV, which is also further supported by the above estimated band gap from absorption spectrum using Tauc plot and is in good agreement with several recently published PL results18,30. Further, a deconvolution analysis of the observed PL spectrum was carried out by fitting with three Gaussian peaks i.e. the neutral exciton (A0), negative trion (A−) and B exciton. The A0 and B exciton peaks are associated with the direct band gap transition at K point in the Brillouin zone, with energy split from the strong valance band spin orbit coupling as shown in Fig. 4b. The deconvolution result of PL spectrum exhibits Ao exciton energy of 1.82 eV21 while A- trion energy has been 1.79 eV18. The PL intensity of Ao is observed to be much higher as compared to A- trion, as shown in Fig. 4b. Moreover, for better understanding of PL emission process as well as dominance of Ao exciton as compared to A- trion in as-synthesized monolayer MoS2, an energy level diagram has been proposed as shown in Fig. 4c. This energy level diagram also helps to understand the difference in PL process between bulk MoS2 indirect transition to monolayer direct transition. The theoretical prediction based on bulk MoS2 models estimates the indirect bandgap of bulk MoS2 as ~ 1.23 eV26. However, in case of monolayer MoS2, it is interesting to know that A excitonic peak originates due to the change of excitonic binding energy or the gap between the lowest conduction band (CB) and the highest valence band at the K point of the Brillouin zone. One remarkable feature could be realized that when the layer thickness decreases from even few layers and bi-layer to monolayer, the PL intensity of A exciton is strongly enhanced, but that of the B exciton remains nearly constant as also experimentally observed by many research groups including our previous work related to quantification of number of layers of MoS2 using PL spectroscopy19. On the other hand, in case of bulk MoS2 the PL intensity of A and B excitons are almost similar31,32. While the presence of strong enhancement of the A exciton in monolayer MoS2 as compared to bulk can be implicit by the indirect to direct bandgap crossover as shown in Fig. 4a as well as in proposed energy level diagram in Fig. 4c, where the stark contrast of B exciton is showing a nearly constant intensity even when the thickness is changed from mono to bi-layer as reported in our previous studies too19. On the ground of experimental observations, the proposed energy level diagram represents the A and B excitonic transitions including the possibility of dominance of the presence of Ao exciton as compared to A− trion defect level which is originated due to charge impurity present in as-synthesized monolayer MoS2. The lesser presence of A− trion defect level exhibits the better crystal quality of as-synthesized monolayer MoS2. Furthermore, the dominance of Ao exciton interaction with conduction band electron of higher energy creates a strong charge-dynamic coupling which is strongly impactful to generate terahertz characteristics as further realized in THz-TDS results. Moreover, the spatial PL intensity distribution and uniformity of individual triangular shaped monolayer MoS2 throughout the surface was examined by using PL mapping technique where, 532 nm diode laser as a source of excitation with spot size of 1 μm was used as shown in Fig. 4d. The PL mapping result reveals that the PL intensity of the as–synthesized monolayer MoS2 is excellent with almost uniform throughout the triangular region33.

PL Characterization and Mechanism. (a) PL spectrum of monolayer MoS2 over 300 nm thick SiO2/Si substrate. (b) Deconvoluted PL spectrum of monolayer MoS2. (c) Proposed energy level diagram. (d) PL mapping of monolayer MoS2 with respect to A excitonic peak, scale bar is mentioned.

Furthermore, the terahertz time-domain spectroscopy (THz-TDS) has been performed to explore the terahertz characteristics of as deposited monolayer MoS2 and bulk MoS2 on sapphire substrate by APCVD technique as shown in Fig. S434. To satisfy the need of highly resistive substrate in order to nullify the conductive losses in substrate35 for THz-TDS measurements, the sapphire substrate has been chosen for growth of monolayer MoS2. The already optimized growth parameters have been used for growth on sapphire substrate as discussed in the experimental part. In order to validate the quality of as grown material on sapphire, optical microscopy and Raman spectroscopy have also been performed on sapphire substrates and shown in Figs. S5 and S6, respectively. A femtosecond (FS) laser in combination with photo conductive switch antennas are used for the generation and detection of terahertz pulses in order to perform THz-TDS on the samples. Briefly, THz-TDS technique employs a FS laser beam, which further splits into two parts. The actual set-up of THz-TDS as shown in Fig. 5a,b, depicts a schematic representation of THz-TDS mechanism. In THz-TDS set-up, the laser beam arrangements have been adapted in two different paths to generate and detect THz. In the first path, the split laser beam travels directly to terahertz emitter where it interacts with (photo conducting antenna) PCA to generate THz pulses, while in the other path, split beam reaches the detector in order to detect the generated THz pulse that passes through the sample (MoS2 on sapphire substrate in this study) (see, Fig. 5b). In such a way detected time-domain terahertz pulses are further converted to frequency domain spectra through Fast Fourier Transformations (FFT) resulting in complex frequency domain spectrum, as represented in the below equation:

Time-domain terahertz spectroscopy set-up. (a) Pictorial view of Time-domain terahertz spectroscopy system and insets show the arrangement of parabolic mirrors and sample holder. (b) Schematic representation of THz-TDS mechanism.

Therefore, THz-TDS can provide information about both amplitude and phase. Further, with suitable referencing, such transmission measurements can provide frequency dependent information related to various optical parameters, such as, conductivity, refractive index, absorption coefficient etc. of the material under study. It is noticeable that the THz-TDS are performed at room temperature in dry atmosphere in order to negate the influence of humidity in atmosphere, hence capturing the genuine responses of MoS2 as closely as possible. The precision of the measurement of time-domain terahertz spectroscopy was calibrated in air as well as with known commercial sample for terahertz spectroscopy in terms of responsivity, transmission and sheet conductivity.

Further, Tinkham approximation has been used for analyzing the behaviors of ultrathin films of monolayer MoS236. Therefore, frequency dependent conductivities are estimated using the following relations:

here FFT: Fast Fourier transformation, T (\({\upomega }\)): Transmission, ns: refractive index of substrate, Z0: vacuum impedance (377 Ω), Esample(\({\upomega }\)): THz EF signal through sample, Esubstrate(\({\upomega }\)): THz EF signal through bare substrate

The observations for time-domain terahertz spectroscopy were carried out in denser areas of triangular shaped monolayers MoS2 (greater than terahertz spot size) which was confirmed through optical microscopy prior to measurement. Figure 6 depicts the terahertz signal transmitted through the monolayer MoS2. The transmitted terahertz pulse through the monolayer MoS2 has been first converted into frequency domain spectra using FFT and analyzed further. THz-TDS measurements of monolayer MoS2 show that monolayer MoS2 can modulate radiations as well as demonstrate certain responsivity in THz region as shown in Fig. 6a–d. The THz pulses transmitted through the monolayer MoS2 on sapphire substrate along with bare sapphire substrate36 are shown in Fig. 6a. However, Fig. 6b is the magnified view of pulses which are shown in Fig. 6a to depict the changes in transmitted pulses closely. Further, THz conductivities extracted using Tinkham relation are shown in Fig. 6d for 0.2–1.2 THz frequency range. Transmission spectrum through monolayer MoS2 demonstrates high transmission of almost 94–97% which is observed due to higher energy bandgap present in monolayer MoS2 as shown in Fig. 6c. The extracted sheet conductivity of APCVD grown monolayer MoS2 turn out to be around 1.3304 × 10−4 to 4.42 × 10−4 S/m for the similar THz frequency range. The unusual variations observed in conductivity may be explained on the basis of Ligand field theory. However, there is no direct evidence reported earlier for the same effects. Generally, this theory results from combining the principles laid out in molecular orbital theory and crystal field theory, which describes the loss of degeneracy of metal d-orbitals in transition metal complexes. It is interesting to observe that a small absorption of THz signal and blue shift were found due to the quantum confinement effect observed in monolayer MoS2. A strong spin–orbit coupling occurred between the conduction band electrons with A0 exciton direct band transition which is also supported by observed PL results as discussed earlier. Furthermore, for better clarity, a plausible mechanism has been proposed to explain the outstanding THz characteristics of atomic thin monolayer MoS2 as compared to bulk MoS2 crystal as shown in Fig. 7. Prior to perform the THz-TDS on bulk MoS2, the purity of crystal has been examined through XRD and Raman spectroscopy techniques as shown in Figs. S7 and S8, respectively. In present investigations, THz beam (with spot size 3–4 mm) is passed through monolayer MoS2 sample on substrate. Simultaneously, substrate is also measured prior to any deposition of monolayer MoS2 on it as shown in Fig. S9. Finally, THz signal passing through (MoS2 + substrate) is normalized with THz signal passed through substrate only. This way, we captured intrinsic true response of monolayer MoS2, which is devoid of any contribution from the substrate. The Fig. 7a–c represents the condition when terahertz signal interacts with bulk MoS2. The bulk MoS2 has lesser transmission of THz signal due to the continuous valance and conduction bands with indirect transition (band gap; Eg = 1.23 eV) which results in larger carrier-carrier scattering (2 ps)37, carrier-phonon scattering (20 ps)37 and intervalley scattering (2.6 ns)37. However, in case of monolayer MoS2, direct transition (band gap; Eg = 1.82 eV) with discreet energy levels are present because of quantum confinement effect, and hence defect assisted scattering (< 500 fs)37 and carrier-phonon scattering (80 ps) 37 are less dominating as shown in Fig. 7d–f. Therefore, transmission and sheet conductivity behave differently in case of thin monolayer MoS2 while it quenches significantly in case of bulk MoS2. Additionally, the terahertz signal is transmitted efficiently through monolayer MoS2 because resonance phenomenon occurs between incident and transmitted terahertz signals which can provide larger room for tunability for future THz applications38. This resonance phenomenon happens since the terahertz signal pulse width better synchronizes with monolayer MoS2 because of intraband direct transition time 350 fs reported9 earlier for monolayer MoS2 which is much smaller than the terahertz signal pulse width as shown in Fig. 7e. However, in case of bulk MoS2, the terahertz pulse does not synchronize with terahertz signal pulse width because of indirect band transition time is in the range of ps which is much larger than the terahertz signal pulse width in the range of fs. This could cause the major loss of terahertz signal in bulk MoS2, as a result the terahertz signal intensity in bulk MoS2 could significantly reduce as shown in proposed mechanism in Fig. 7b and major loss of terahertz signal, as also observed by other research groups for bulk MoS239. We also performed two more measurements for monolayer MoS2 at different denser locations to ensure the successive repeatability of results as shown in Fig. S9. Thus, the time-domain spectroscopy results of monolayer MoS2 quantum material legitimate its potential use in wireless communication and also ignite us further to do more study for ultrafast, pump probe and 2D coherent spectroscopy to design the suitable next generation THz devices which will be our forth coming focus of study.

Time-domain terahertz spectroscopy. (a) THz signal transmitted through monolayer MoS2 on sapphire substrate. (b) Magnified view of transmitted THz pulse. (c) Transmitted THz amplitude through monolayer MoS2 grown on sapphire substrate. (d) Extracted sheet conductivity of monolayer MoS2 on sapphire substrate in THz frequency domain.

Comparative study of THz characteristics of bulk and monolayer MoS2. (a) THz signal incident on bulk MoS2. (b) THz signal transmitted through bulk MoS2. (c) Energy level diagram of bulk MoS2. (d) THz signal incident on monolayer MoS2. (e) THz signal transmitted through monolayer MoS2. (f) Energy level diagram of monolayer MoS2.

A successful strategy has been proposed to synthesize high-quality monolayer MoS2 using indigenously developed APCVD set-up at CSIR-NPL, New Delhi, India. The optical and spectroscopic characterizations of monolayer MoS2 have been qualitatively validated through optical microscopy, Raman, UV–Vis and PL spectroscopic techniques which further quantified the deposited MoS2 as monolayer in nature. Moreover, the uniformity and spatial intensity distribution throughout the surface of monolayer MoS2 crystals was ensured through PL and Raman mapping and also the different in-plane and out-of-plane vibrations of Mo and S atoms were explored through mapping E12g at 381.57 cm−1 and A1g at 401.04 cm−1, respectively. The morphologies and average lateral sizes of ~ 21.34 µm of triangular shaped monolayer MoS2 was confirmed through FESEM. Moreover, THz-TDS studies reveal conductivities in the range of 1.3304 × 10–4 – 4.42 × 10–4 S/m for monolayer MoS2 within the frequency range of 0.2–1.2 THz frequency domain. The unexplored terahertz characteristics of monolayer MoS2 was explained in details and successfully proposed a plausible mechanism to explore the optical absorption introduced by electron-photon interaction in monolayer MoS2 including the role of exciton carrier dynamics of monolayer MoS2 due to quantum confinement effect and supported the argument through observed PL and terahertz characteristics. Thus, the obtained terahertz optoelectronic characteristics show potential of monolayer MoS2 as an impactful quantum material as compared to bulk MoS2 to participate in the development of next generation compact terahertz communication devices.

An indigenously laboratory developed APCVD set was used for the synthesis of monolayer MoS2 as shown in Fig. 1. The APCVD growth of monolayer MoS2 was optimized by varying the growth parameters such as gas flow, amount of precursors, distance between ceramic boats and heating rate etc.40. This process involves the evaporation of both metal oxide and chalcogenide precursors at different growth temperatures in horizontal quartz tube furnace. Several statistical runs of APCVD have been performed to optimize the condition on the basis of above mentioned parameters. The optimum condition was achieved with 15 mg of MoO3 (99.9%, Sigma Aldrich) and 100 mg of Sulfur (S) (CDH Delhi) in powder forms in ceramic boats (length 9 cm each) and placed in heating zone of furnace (24 cm distant from each other) in a quartz tube (specifications: 12.27 cm length, 6 cm inner diameter, 6.5 cm outer diameter) in horizontal split furnace. Further, cleaned SiO2/Si substrates were kept facing down on ceramic boat inside the furnace. Before heating the tube, it was evacuated with rotary pump for vacuum pressure of 4.2 torr to avoid any contamination of Oxygen during the growth. Further, the tube was purged with 480 sccm of Argon (Ar) gas for removal of different kinds of absorbed contaminants in tube such as moisture, dust etc.16. This inert environment of tube avoids any reaction with foreign particle impurities during the growth process. Heating ramp was set up for 30 min and was completed in two sequential steps21,40,41. In first step, gas flow was maintained same as before (480 sccm) up to 300 °C with a ramping rate of 14 °C/min. In second step, the gas flow rate was reduced to 120 sccm and ramping rate was allowed to increase up to 23 °C/min. Then, the vapor phase reaction started and growth was performed for 5 minutes41 at 655 °C. After growth, the furnace was allowed to cool naturally. Flow of inert gas was maintained inside the tube until the furnace cools down to 100 °C16,34. After the successful deposition of the monolayer MoS2 on SiO2/Si substrate, the substrate color was observed different from its body color prior to perform APCVD process. After successful deposition, the monolayer MoS2 was analyzed under optical microscope and other characterization techniques to validate its monolayer nature and quality. The optimum conditions were also examined through several sequential statistical runs and ultimately developed the strategy to grow highly reproducible monolayer MoS2 using indigenously developed APCVD.

To check the quality and purity of precursors prior to monolayer growth process using APCVD method, X-ray diffraction (XRD) has been performed for commercially purchased MoO3powder, S powder and MoS2 crystal through Rigaku made Mini Flex II X-ray diffractometer with Cu Kα1 (λ = 1.5418Å) radiation source. In order to visualize the synthesized monolayer MoS2 over the SiO2/Si substrate (GMS-India), optical microscopy is carried out. The LEXT 3D measuring laser microscope OLS5100 having the objective lenses MPLAPON50XLEXT, MPLAPON100XLEXT with NA and working distance of 0.95 and 0.35 mm, respectively is utilized in the bright field mode. Field emission scanning electron microscopy (FESEM) was used to investigate the surface morphology with Carl ZEISSSUPRA40 VP. Further, the Raman spectroscopy of monolayer MoS2 and bulk MoS2 crystal was performed using Renishaw inViaTM confocal Raman microscope (magnification: 50x, 100x) source of excitation laser wavelength was selected 532 nm/2.33 eV energy in backscattering mode at room temperature. UV–visible absorption spectrum of the monolayer has been recorded using a UV–Vis spectrometer (AvaLight-DH-S-BAL) to observe the excitonic states. The complementary PL spectroscopy was carried out using same instrument of Raman with configurational change at room temperature. The Raman and PL mappings were also performed with same Renishaw inViaTM confocal equipment at different spatial mapping configurations. The terahertz characteristics of monolayer MoS2 was extensively examined with the help of THz- TDS using TOPTICA FemtoErb THz FD6.5 (specifications: laser radiation 1560 nm, repetition rate 100 MHz, laser power 80mW).

The datasets used and/or analysed during the current study available from the corresponding author on reasonable request.

Pawar, A. Y. et al. Terahertz technology and its applications. Drug Invent. Today 5, 157–163 (2013).

Article Google Scholar

Serghiou, D. et al. Terahertz channel propagation phenomena, measurement techniques and modeling for 6G wireless communication applications: A survey, open challenges and future research directions. IEEE Commun. Surv. Tutor. 24, 1957–1996 (2022).

Article Google Scholar

Koelemeij, J. et al. A hybrid optical—Wireless network for decimetre-level terrestrial positioning. Nature 611, 473–478 (2022).

Article ADS CAS PubMed Google Scholar

Chowdhury, M. Z. et al. 6G wireless communication systems: applications, requirements, technologies, challenges, and research directions. IEEE Open J. Commun. Soc. 1, 957–975 (2020).

Article Google Scholar

Devi, K. M., Jana, S. & Chowdhury, D. R. Topological edge states in an all-dielectric terahertz photonic crystal. Opt. Mater. Express 11(8), 2445–2458 (2021).

Article ADS Google Scholar

Goel, N. & Kumar, M. 2D materials for terahertz application. Nano Express 2, 031001 (2021).

Article ADS Google Scholar

Abohmra, A. et al. Two-dimensional materials for future terahertz wireless communications. IEEE Open J. Antennas Propag. 3, 217–228 (2022).

Article Google Scholar

Shi, J. et al. THz photonics in two dimensional materials and metamaterials: Properties, devices and prospects. J. Mater. Chem. C 6, 1291–1306 (2018).

Article CAS Google Scholar

Docherty, C. J. et al. Ultrafast transient terahertz conductivity of monolayer MoS2 and WSe2 grown by chemical vapor deposition. ACS Nano 8, 11147–11153 (2014).

Article CAS PubMed Google Scholar

Splendiani, A. et al. Emerging photoluminescence in monolayer MoS2. Nano Lett. 10, 1271–1275 (2010).

Article ADS CAS PubMed Google Scholar

Wei, L. et al. Electronic and elastic properties of MoS2. Phys. B 405, 2498–2502 (2010).

Article ADS Google Scholar

Yue, Q. et al. Mechanical and electronic properties of monolayer MoS2 under elastic strain. Phys. Lett. A 376, 1166–1170 (2012).

Article ADS CAS Google Scholar

Ermolaev, G. A. et al. Broadband optical properties of monolayer and bulk MoS2. npj 2D Mater. Appl. 4, 21 (2020).

Article CAS Google Scholar

Mak, K. et al. Atomically thin MoS2: A new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).

Article ADS PubMed Google Scholar

Bradford, J. Growth and Characterisation of Two-Dimensional Materials and Their Heterostructures on SiC. PhD Thesis ,Queensland University of Technology (2019).

Guo, Y. et al. MoO3–MoS2 vertical heterostructures synthesized via one-step CVD process for optoelectronics. 2D Materials 8, 035036 (2021).

Article CAS Google Scholar

Luo, B. Chemical vapor deposition of clean and pure MoS2 crystals by inhibition of MoO3−x intermediates. CrystEngComm 23, 146–152 (2020).

Google Scholar

Papanai, G. S. et al. New insight into the growth of monolayer MoS2 flakes using an indigenously developed CVD setup: A study on shape evolution and spectroscopy. Mater. Chem. Front. 5, 5429–5441 (2021).

Article CAS Google Scholar

Papanai, G. S. et al. Qualitative analysis of mechanically exfoliated MoS2 nanosheets using spectroscopic probes. J. Phys. Chem. C 123, 27264–27271 (2019).

Article CAS Google Scholar

Li, F. et al. Anomalous lattice vibrations of CVD-grown monolayer MoS2 probed using linear polarized excitation light. Nanoscale 11, 13725–13730 (2019).

Article CAS PubMed Google Scholar

Han, T. et al. Probing the growth improvement of large-size high quality monolayer MoS2 by APCVD. Nanomaterials 9, 433 (2019).

Article CAS PubMed PubMed Central Google Scholar

Li, X. et al. Isotope-engineering the thermal conductivity of two-dimensional MoS2. ACS Nano 13, 2481–2489 (2019).

CAS PubMed Google Scholar

Yu, Y. et al. Controlled scalable synthesis of uniform, high-quality monolayer and few-layer MoS2 films. Sci. Rep. 3, 1–6 (2013).

Article Google Scholar

Wang, Q. et al. Wafer-scale highly oriented monolayer MoS2 with large domain sizes. Nano Lett. 20, 7193–7199 (2020).

Article ADS CAS PubMed Google Scholar

Yalon, E. et al. Temperature-dependent thermal boundary conductance of monolayer MoS2 by Raman thermometry. ACS Appl. Mater. Interfaces 9, 43013–43020 (2017).

Article CAS PubMed Google Scholar

Cheiwchanchamnangij, T. & Lambrecht, W. R. J. P. R. B. Quasiparticle band structure calculation of monolayer, bilayer, and bulk MoS2. Phys. Rev. B 85, 205302 (2012).

Article ADS Google Scholar

Mueller, T. & Malic, E. J. N. D. M. Exciton physics and device application of two-dimensional transition metal dichalcogenide semiconductors. npj 2D Mater. Appl. 2, 1–12 (2018).

Article ADS Google Scholar

Steinhoff, A. et al. Efficient excitonic photoluminescence in direct and indirect band gap monolayer MoS2. Nano Lett. 15, 6841–6847 (2015).

Article ADS CAS PubMed Google Scholar

Kim, J. G. et al. Effect of interlayer interactions on exciton luminescence in atomic-layered MoS2 crystals. Sci. Rep. 6, 1–7 (2016).

CAS Google Scholar

Chowdhury, S. et al. Two-step growth of uniform monolayer MoS2 nanosheets by metal-organic chemical vapor deposition. ACS Omega 6, 10343–10351 (2021).

Article CAS PubMed PubMed Central Google Scholar

Kim, T. & Shin, J. C. Structural defects in a nanomesh of bulk MoS2 using an anodic aluminum oxide template for photoluminescence efficiency enhancement. Sci. Rep. 8, 6648 (2018).

Article ADS PubMed PubMed Central Google Scholar

Dhakal, K. et al. Confocal absorption spectral imaging of MoS2: Optical transitions depending on the atomic thickness of intrinsic and chemically doped MoS2. Nanoscale 6, 13028–13035 (2014).

Article ADS CAS PubMed Google Scholar

Sun, L. et al. Vacuum level dependent photoluminescence in chemical vapor deposition-grown monolayer MoS2. Sci. Rep. 7, 1–9 (2017).

Article ADS Google Scholar

Wen, H. et al. Magneto-optical properties of monolayer MoS2-SiO2/Si structure measured via terahertz time-domain spectroscopy. Nano Select 2, 90–98 (2021).

Article CAS Google Scholar

Jana, A. et al. External bias dependent dynamic terahertz propagation through BiFeO3 film. Nanotechnology 33, 325202 (2022).

Article Google Scholar

Wang, C. et al. Substrate-induced electronic localization in monolayer MoS2 measured via terahertz spectroscopy. Opt. Lett. 44, 4139–4142 (2019).

Article ADS CAS PubMed Google Scholar

Shi, H. et al. Exciton dynamics in suspended monolayer and few-layer MoS2 2D crystals. ACS Nano 7, 1072–1080 (2013).

Article CAS PubMed Google Scholar

Shi, J. et al. Room temperature terahertz electroabsorption modulation by excitons in monolayer transition metal dichalcogenides. Nano Lett. 20, 5214–5220 (2020).

Article ADS CAS PubMed Google Scholar

Yan, X. et al. Dielectric property of MoS2 crystal in terahertz and visible region. Appl. Opt. 54, 6732–6736 (2015).

Article ADS CAS PubMed Google Scholar

Tummala, P. et al. Application-oriented growth of a molybdenum disulfide (MoS2) single layer by means of parametrically optimized chemical vapor deposition. Materials (Basel) 13, 2786 (2020).

Article ADS CAS PubMed Google Scholar

Singh, A. et al. NaCl-assisted substrate dependent 2D planar nucleated growth of MoS2. Appl. Surf. Sci. 538, 148201 (2021).

Article CAS Google Scholar

Download references

Authors acknowledge the Director, Prof. Venugopal Achanta, CSIR-NPL, for providing the research facility for the mission mode project on "Metrology of 2D quantum materials". We are thankful to Mr. Anish Bhargava and Anish Alam for their continuous support in the Optical Microscopy facility. We thank Dr. V.P.S. Awana for providing the XRD facility. We also thank Dr. J.S. Tawale for FESEM characterization. The authors, S.S and P.C. acknowledge to University Grant Commission (UGC), India and CSIR, India for their UGC-SRF and CSIR-JRF research fellowships, respectively. Authors SR and DRC acknowledges partial supports from 58/14/32/2019-BRNS/11090. Authors acknowledge CIF, Jamia Millia Islamia for providing the Raman and PL measurements.

Photonic Materials Metrology Sub Division, Advanced Materials and Device Metrology Division, CSIR-National Physical Laboratory, Dr. K. S. Krishnan Road, New Delhi, 110012, India

Saloni Sharma, Pooja Chauhan, Utkarsh Raj, Shubhda Srivastava & Bipin Kumar Gupta

Academy of Scientific and Innovative Research (AcSIR), Ghaziabad, 201002, India

Saloni Sharma, Pooja Chauhan & Bipin Kumar Gupta

Mahindra University, Bahadurpally, Hyderabad, Telangana, 500043, India

Shreeya Rane & Dibakar Roy Chowdhury

Centre for Interdisciplinary Research in Basic Sciences, Jamia Millia Islamia, Jamia Nagar, New Delhi, 110025, India

Z. A. Ansari

You can also search for this author in PubMed Google Scholar

S.S. has conceived the concepts, investigations, methodology, analysis and writing draft of the research. P.C. has done some analysis part of the research. S.R. performed the time-domain terahertz spectroscopy measurements as well as helped in analyzation part. U. R. constructed the 3D view schematic representations of experiment. S.S. has helped in the fabrication of the samples and reviewed the writing part. Z.A.A. carried out Raman & PL measurements also edited and reviewed the project. D.R.C. provided the facility of time-domain terahertz spectroscopy measurement also edited and reviewed the writing part. B.K.G. conceived, conceptualized, edited, reviewed and supervised the project. All authors contributed to the preparation of the manuscript. Availability of Data and Materials: The datasets used and/or analysed during the current study available from the corresponding author on reasonable request.

Correspondence to Bipin Kumar Gupta.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Sharma, S., Chauhan, P., Rane, S. et al. New insights into APCVD grown monolayer MoS2 using time-domain terahertz spectroscopy. Sci Rep 13, 4146 (2023). https://doi.org/10.1038/s41598-023-31102-z

Download citation

Received: 20 December 2022

Accepted: 06 March 2023

Published: 13 March 2023

DOI: https://doi.org/10.1038/s41598-023-31102-z

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Cannula: Definition, types, purpose, and more

Tech Talk: How to Prevent Potentially Damaging Drip, Drip, Drips

News

New insights into APCVD grown monolayer MoS2 using time